Title: THERMAL PROPERTIES OF HIGH DENSITY POLYETHYLENE-KENAF CELLULOSE COMPOSITES
Page Range: p.257-261
Author(s): Tajeddin B; Abdulah L C
File size: 148K
Download the pdf (subscribers only)
Buy the pdf (non-subscribers)
Journal: Polymers and Polymer Composites
Issue Year: ppc
Volume: 18
Issue No: No.5
Abstract
Biocomposites of high density polyethylene (HDPE) and kenaf cellulose (KC) with polyethylene glycol (PEG) have been prepared by melt blending and compression moulding. The optimum temperature and reaction period for blending KC with HDPE were 145 °C and 12 minutes with rotation speed of 30 rpm, respectively. The effects of composition on the thermal properties of HDPE-KC biocomposites were investigated using TGA and DSC. Each sample of HDPE-KC biocomposites was subjected to heating programs between 35-600 °C for TGA, and the DSC analysis was determined under heating cycles of 25-600 °C. The results from TGA and DSC indicated that by increasing the KC content, the thermal stability was slightly improved. The melting temperature for all the composites was less than the melting point of KC (148.70 °C), and almost the same as that of HDPE (130.38 °C). Therefore no significant change in the melting temperature resulted from adding KC to the HDPE matrix. However, HDPE’s presence surrounding the KC fibres, prevented water from reaching the cellulose fibre particles, thus reducing the water content in the composite; hence a significant advantage of forming KC composites with hydrophobic HDPE is that it helps to make the cellulose hydrophobic instead of hydrophilic. 15 Refs.
Related reading
More journal reading and science coverage connected to this topic.
Curing residual strain monitoring of carbon fiber reinforced polymer composite using notched long-period fiber grating
Title: Curing residual strain monitoring of carbon fiber reinforced polymer composite using notched long-period fiber grating Page Range: p.27-34 Author(s): Ke-Ping Ma; Chao-Wei Wu;…
Mechanical properties of glass bead-modified polymer composite
Title: Mechanical properties of glass bead-modified polymer composite Page Range: p.35-44 Author(s): Tsung-Han Hsieh; Ming-Yuan Shen; Yau-Shian Huang; Qi-Qian He; Hsuan-Chih Chen File size:…
The effect of MBS toughening for mechanical properties of wood-plastic composites under environmental ageing
Title: The effect of MBS toughening for mechanical properties of wood-plastic composites under environmental ageing Page Range: p.45-58 Author(s): Chin-Hsing Chen; Chin-Lung Chiang; Wei-Jen…