# FABRICATION, STRUCTURAL MORPHOLOGY AND THERMAL ENERGY STORAGE/RETRIEVAL OF ULTRAFINE PHASE CHANGE FIBRES CONSISTING OF POLYETHYLENE GLYCOL AND POLYAMIDE 6 BY ELECTROSPINNING

> Title: FABRICATION, STRUCTURAL MORPHOLOGY AND THERMAL ENERGY STORAGE/RETRIEVAL OF ULTRAFINE PHASE CHANGE FIBRES CONSISTING OF POLYETHYLENE GLYCOL AND POLYAMIDE 6 BY ELECTROSPINNING Page Range: p.525-532 Author(s): Yibing Cai; Xue Zong; Heng Ban; Qian Liu; Hui Qiao; Qufu Wei; Yong Zhao; Hao Fong...

Canonical URL: https://polymerjournals.com/fabrication-structural-morphology-and-thermal-energy-storage-retrieval-of-ultrafine-phase-change-fibres-consisting-of-polyethylene-glycol-and-polyamide-6-by-electrospinning/
Published: 2013-08-01T00:00:00+00:00
Categories: Polymers and Polymer Composites

**Title: FABRICATION, STRUCTURAL MORPHOLOGY AND THERMAL ENERGY STORAGE/RETRIEVAL OF ULTRAFINE PHASE CHANGE FIBRES CONSISTING OF POLYETHYLENE GLYCOL AND POLYAMIDE 6 BY ELECTROSPINNING**
 Page Range: p.525-532
 Author(s): Yibing Cai; Xue Zong; Heng Ban; Qian Liu; Hui Qiao; Qufu Wei; Yong Zhao; Hao Fong
 File size:
 ![](http://dload.gif) [Download the pdf](http://journals.asp?Page=111&JournalDownload=ON&JournalType=ppc&JournalIssue=ppc21-8&JournalID=102062&JIP=) (subscribers only)
 ![](http://handbuy.gif) Buy the pdf (non-subscribers)
 Journal: Polymers and Polymer Composites
 Issue Year: ppc
 Volume: 21
 Issue No: No.8

**Abstract**
 This study aimed at the development and characterization/evaluation of polyethylene glycol (PEG) encapsulated in supporting polymer matrices (e.g., electrospun nanofibres) as innovative form-stable phase change materials (PCMs) for storage and retrieval of thermal energy. Ultrafine phase change fibres consisting of PEG (acting as phase change materials) and polyamide 6 (PA6, acting as supporting materials) were successfully fabricated by electrospinning technique. The effects of PEG amount and two different molecular weights (Mn) of PEG on structural morphology and thermal energy storage/retrieval property of PEG/PA6 ultrafine phase change fibres were systematically studied by scanning electron microscopy (SEM) and differential scanning calorimetry (DSC), respectively. The SEM images showed that neat PA6 nanofibres were smooth with cylindrical shape, but the tubercles and/or beads in fibres were observed for PEG/PA6 ultrafine phase change fibres with increasing PEG amount and higher molecular weight of PEG. The average fibre diameters ranged from about 80 to 150 nm and increased with increasing the PEG amount and molecular weight of PEG, which resulted from the increased viscosity and decreased conductivity of composite spin dopes. The DSC results indicated that the enthalpies of melting and crystallisation of PEG/PA6 ultrafine phase change fibres increased with increasing PEG amount, and were lower than those of neat PEG powders. 32 Refs.

---