# A novel approach for fabricating poly-l-lactide materials by onestep bulk polymerization

> Title: A novel approach for fabricating poly-l-lactide materials by onestep bulk polymerization Page Range: p.249-254 Author(s): Zhiyuan Peng; Zhiping Li; Fan Zhang; Xiaochun Peng File size: Download the pdf (subscribers only) Buy the pdf (non-subscribers) Journal: Polymers and Polymer Composites Issue Year:...

Canonical URL: https://polymerjournals.com/a-novel-approach-for-fabricating-poly-l-lactide-materials-by-onestep-bulk-polymerization/
Published: 2016-04-01T00:00:00+00:00
Categories: Polymers and Polymer Composites

**Title: A novel approach for fabricating poly-l-lactide materials by onestep bulk polymerization**
 Page Range: p.249-254
 Author(s): Zhiyuan Peng; Zhiping Li; Fan Zhang; Xiaochun Peng
 File size:
 ![](http://dload.gif) [Download the pdf](http://journals.asp?Page=111&JournalDownload=ON&JournalType=ppc&JournalIssue=ppc24-4&JournalID=102700&JIP=) (subscribers only)
 ![](http://handbuy.gif) Buy the pdf (non-subscribers)
 Journal: Polymers and Polymer Composites
 Issue Year: ppc
 Volume: 24
 Issue No: No.4

**Abstract**
 Poly-L-lactide (PLLA) is one of the most significant members of a group of bioabsorbable polymers. A new approach for fabricating PLLA material was investigated by one-step bulk polymerisation. The focus of this paper was on the effect of reaction temperature and reaction time on the weight-average molar mass, the polydispersity index (PDI), and the flexural strength and modulus. Gel permeation chromatography (GPC), scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR) and mechanical properties measurements were used to characterise the products. It was found that the optimal reaction conditions were at 140 degC for 24 h, under which the highest (5.02 x 105 Da) and the lowest PDI (1.16) were reached. In addition this material had the highest flexural strength and modulus, 74.58 plus/minus 2.35 MPa and 1.62 plus/minus 0.14 GPa, respectively. 19 Refs.

---